Two-component cold-curing construction sealant for deformation joints “Izol-11” is formulated on the base of polyurethane polymer.
Consist of two components – main paste and curing agent. After mixing makes thixotropic paste, which is easy in handling. After curing it becomes elastic resin-like material with high deformation and tensile strength characteristics, resistant to vibration and atmospheric factors, with perfect adhesion to all construction materials.
Package: plastic drums 15 kg.
APPLICATION FIELDS
- Sealing of construction joints with up to 50% deformation.
- Sealing of concrete stone joints.
- Sealing of other joints and cracks.
“IZOL-11” SEALANT PROPERTIES
- Consistency – thixotropic paste, easy in handling.
- Good adhesion to all construction materials (concrete, polymer concrete, wood, metal, glass, stone).
- No contraction, does not contain solvents.
- Workable under temperatures from- 50 оС to +70 оС.
- Resistant to climatic factors.
- Colorable.
- Life duration over 10 years.
TECHNICAL PROPERTIES
|
Parameter |
Norms |
|
Appearance |
Light-grey thixotropic paste |
|
Relative tensile strength at break, MPa, min |
0,5 |
|
Elastic module at 100% elongation, mPA, max |
0,4 |
|
Flow resistance, mm, max |
2 |
|
Relative elongation at break, %, min |
400 (on sample joints) 600 (on blades) |
|
Breakage character |
Cohesion |
|
Pot-life under+23оС, hours |
2 – 24 |
|
Handling temperature range |
from -15 till +40оС |
|
Density, kg/m3 |
1450 |
HANDLING INSTRUCTIONS
Sealant components are mixed just before use by hand mixing or spiral drill (in order not to create extra air bubbles speed of drill should be not more than 300 rev/min) till getting homogeneous paste, but not more than 5 minutes. Quality of sealant depends on mixing accuracy. Partial mixing is not recommended, as there is possibility of wrong measurement of components.
Mixing with solvents is strictly prohibited, as it leads to loss of thixotropy and other properties, cause shrinking and cracks.
Sealant layer should be not more than 3-4 mm.
Viscosity of sealant components increase under low temperatures. Mixing and storage is recommended in heated buildings.
Two-component construction sealant based on thiol-content AR-polymer used for sealing deformation joints in panel house construction, in underground and over ground concrete, ferroconcrete constructions with maximum joint deformation 25%.
Two component universal construction sealant based on thiol-contented “AR-polymer” for sealing, waterproofing, protection against corrosion of joints (including metal parts) of underground and over ground constructions from concrete, foamed, ferroconcrete, brick.
We can select materials for your sphere with the possibility of adapting the products to your individual requirements.
Describe your task and we will offer the perfect option. Our specialists will consult and send calculations or a commercial offer for your task to the indicated contact addresses.